IRRAX SLEEVE SCM2
■ 外層熱收縮套管性能 OUTER LAYER PROPERTIES
|
|
Test Method |
Requirment |
Typical Data |
|
Tensile Strength |
ASTM D 638 |
10.0 MPa min2 |
21.7 Mpa |
|
Ultimate Elongation |
ASTM D 638 |
350% min |
568% |
|
Accelerated Aging :at 150℃ for 168 hours Tensile Strength Ultimate Elongation |
ASTM D 638 ASTM D 638 |
8.0Mpa min 300% min |
23.5 Mpa 532% |
|
Low Temperature Flexibility :at -55℃ for hour |
ASTM b 2671 |
|
No Cracking |
|
Hardness |
ASTM D 2240 (type D) |
|
41 |
|
Volume Resistivity |
ASTM D 876 |
1×1013Ω-cm min |
2×1014Ω-cm |
|
Dielectric Constant |
IEC250 |
|
4.1 |
|
Shrinking Temperature (Start/Finish) |
|
|
70℃/90℃ |
|
Tracking Resistance |
ASTM D 2303 |
|
Pass At 2.75 KV for 60 minutes |
|
WeatherResistance :for 4,000hours Tensile Strength / UItimate EIongation |
JIC A 1415 (Type WS) |
|
94%/91% of the value obtained unweathered sample |
■
SIZES
|
Trade size |
Inside Diameter as Supplied 【MM】 (min ) |
Inside Diameter after Shrinkage 【mm】 (max.) |
Wall Thickness after Shrinkage 【mm】 (nominal..) |
Unit Length 【mm】 (min.) |
|
04-1220 |
10.2 |
3.80 |
1.50 |
1220 |
|
07-1220 |
19.0 |
5.60 |
2.00 |
1220 |
|
11-1220 |
28.0 |
9.5 |
2.00 |
1220 |
|
13-1220 |
33.0 |
10.2 |
2.00 |
1220 |
|
15-1220 |
38.1 |
12.7 |
2.30 |
1220 |
|
17-1220 |
44.0 |
14.0 |
2.30 |
1220 |
|
20-1220 |
52 |
18.2 |
2.30 |
1220 |
|
27-1220 |
70 |
25.5 |
2.30 |
1220 |
|
35-1220 |
90 |
30.0 |
2.50 |
1220 |
|
50-1220 |
125 |
40.0 |
2.50 |
1220 |